Full-Spectrum Cannabis Extract Microdepots Support Controlled Release of Multiple Phytocannabinoids for Extended Therapeutic Effect
Department of Polymers and Plastics Engineering, Shenkar College of Engineering, Design and Art, Ramat-Gan 52526, Israel
The Laboratory of Cancer Biology and Cannabinoid Research, Department of Biology, Technion-Israel Institute of Technology, Haifa 320003, Israel
*Email: dmeiri@technion.ac.il (D.M.).*Email: lewitus@shenkar.ac.il (D.Y.L.).Abstract
The therapeutic effect of the Cannabis plant largely depends on the presence and specific ratio of a spectrum of phytocannabinoids. Although prescription of medicinal Cannabis for various conditions constantly grows, its consumption is mostly limited to oral or respiratory pathways, impeding its duration of action, bioavailability, and efficacy. Herein, a long-acting formulation in the form of melt-printed polymeric microdepots for full-spectrum cannabidiol (CBD)-rich extract administration is described. When injected subcutaneously in mice, the microdepots facilitate sustained release of the encapsulated extract over a two-week period. The prolonged delivery results in elevated serum levels of multiple, major and minor, phytocannabinoids for over 14 days, compared to Cannabis extract injection. A direct analysis of the microdepots retrieved from the injection site gives rise to an empirical model for the release kinetics of the phytocannabinoids as a function of their physical traits. As a proof of concept, we compare the long-term efficacy of a single administration of the microdepots to a single administration of Cannabis extract in a pentylenetetrazol-induced convulsion model. One week following administration, the microdepots reduce the incidence of tonic-clonic seizures by 40%, increase the survival rate by 50%, and the latency to first tonic-clonic seizures by 170%. These results suggest that a long-term full-spectrum Cannabis delivery system may provide new form of Cannabis administration and treatments.
1Introduction
A central principle underlying the use of whole-plant medicines is that herbs are inherently polypharmaceutical. The potential synergy between the vast number of active ingredients contained in herbs has garnered attention in the phytomedicine field in recent years. Of all the plant species with therapeutic properties, Cannabis is one of the most versatile in terms of its phytochemistry.1−3 More than 500 natural compounds belonging to a broad range of chemical classes have been identified or isolated from Cannabis.4,5 The most abundant are the phytocannabinoids (plant-derived cannabinoids), a family of terpenophenolic compounds uniquely produced by the plant as secondary metabolites.6,7 Gill et al.,8 showed that the activity of Δ9-trans-tetrahydrocannabinol (Δ9-THC), the primary active ingredient of Cannabis, is influenced by other compounds present in the plant, promoting the notion of phytochemical synergy in Cannabis pharmacology.9−12 Gallily et al.,13 reported that the bell-shaped dose–response of purified CBD, another major constituent of Cannabis, is partially alleviated by other phytocannabinoids or noncannabinoids present in the plant. Recently, it was demonstrated that CBD-rich extracts of Cannabis have a superior therapeutic profile for treating refractory epilepsy compared to the isolated cannabinoid.14 These results were supported by the finding that different high-CBD containing Cannabis strains produced different anticonvulsant properties in a pentylenetetrazol (PTZ) test in mice, despite having similar CBD content.5 These differences may arise from pharmacokinetic and pharmacodynamic drug interactions, whose combined therapeutic effects are greater than the sum of their parts.4,9,15,16
In recent years, Cannabis use for medical purposes continues to evolve, as shown by the growing number of states now permitting its administration for a variety of conditions, including chronic pain, cancer associated pain, chemotherapy-induced nausea and vomiting, spacticity associated with multiple scelerosis, Parkinson’s disease, post-traumatic stress disorder, and intractable epilepsy.12,17 Currently, the administration of whole-plant Cannabis is mainly through inhalation pathways, via vaporization or smoking, or by oral ingestion of edible products.18,19 Such consumption sharply increases the therapeutic ingredient levels in the bloodstream and is followed by a short therapeutic action period, lasting no longer than several hours.12,20,21 In addition, phytocannabinoids are lipophilic molecules with low aqueous solubility and susceptibility to degradation, limiting their oral bioavailability. Furthermore, phytocannabinoids absorption is highly dependent on various factors, such as their lipophilic nature, whether the patient had eaten recently, or inhalation conditions.10,12,22 These limiting factors may be overcome via the development of novel dosage forms that are specifically designed to improve the therapeutic efficacy of active substances.10,23
Polymeric microspheres that are employed to encapsulate, protect, and deliver pharmaceuticals in a rate-controlled manner are potentially an attractive dosage form. In these systems, the polymer matrix acts as a carrier that modulates drug release kinetics, significantly extending its residence time and bioavailability, while reducing plasma levels fluctuations and administration frequency.24,25 Several polymeric systems based on poly(lactic-co-glycolic acid) and polycaprolactone (PCL) have been developed in recent years for long-term delivery of CBD, Δ9-THC and the cannabinoid derivative 1-naphthalenyl[4-(pentyloxy)-1-naphthalenyl]methanone (CB13). In vitro, these systems demonstrated sustained release over a two to three week period,26−29 and inhibition of cancer cell proliferation.27,28 In addition, the ability of the polymeric carriers to improve oral absorption22 and extend the pain-relieving effect of CB1330 has been shown in vivo. Moreover, the continuous release of CBD or Δ9-THC reduced the growth of glioma xenografts in tumor-bearing mice,31 and the incorporation of CBD-loaded microspheres in an osteoconductive scaffold improved bone healing.32 However, the encapsulation and delivery of the whole Cannabis plant extract, critical for exploiting synergistic effects, using polymeric carriers has not been reported. In the present study, we aimed to develop polymer-based microdepots as a controlled-release Cannabis formulation. To this end, PCL microdepots loaded with whole-plant medicinal Cannabis extract were produced via melt printing and characterized in terms of physiochemical characteristics, encapsulation efficiency and release behavior in vitro and in vivo. Furthermore, the release of phytocannabinoids into the systemic circulation and its effect on PTZ-induced convulsions in a mouse model was compared to a bolus of pure Cannabis extract as a proof of concept for the therapeutic potential of the microdepots.
2Materials and Methods
2.1Materials
PCL (Mw ∼ 14 000), carboxymethylcellulose (CMC), Tween 20, cremophor, phosphate buffered saline (PBS, pH 7.4), liquid chromatography–mass spectrometry (LC/MS) grade acetic acid, and high-performance liquid chromatography (HPLC) grade dichloromethane were purchased from Sigma-Aldrich (Rehovot, Israel). LC/MS grade acetonitrile, methanol, and water, and HPLC grade ethanol were obtained from Mercury Scientific and Industrial Products Ltd. (Rosh Haayin, Israel) or Bio-Lab Ltd. (Jerusalem, Israel). (−)-trans-Δ9-tetrahydrocannabinolic acid (Δ9-THCA), cannabidiolic acid (CBDA), cannabigerolic acid (CBGA), cannabichromenic acid (CBCA), cannabinolic acid (CBNA), cannabidivarinic acid (CBDVA), Δ9-THC, CBD, cannabigerol (CBG), cannabichromene (CBC), CBN, (−)-trans-Δ9-tetrahydrocannabivarin (Δ9-THCV), cannabidivarin (CBDV), cannabichromevarin (CBCV), Δ9-THC-d3, CBD-d3, and CBN-d3 were purchased from Sigma-Aldrich (Rehovot, Israel). All the phytocannabinoid standards were of analytical grade (>98%).
2.2Cannabis Extraction and Analysis
Air-dried medical Cannabis female flowers were ground to a fine powder using an electrical grinder, and heat-decarboxylated in an oven at 130 °C for 1 h. Approximately 30 g of the decarboxylated flowers were accurately weighed and extracted with 300 mL ethanol. Samples were sonicated in an ultrasonic bath for 30 min and then agitated in an orbital shaker at 25 °C for 15 min. Samples were then filtered under pressure through Whatman No. 4 filter paper and the ethanol was evaporated at 38 °C under reduced pressure using a rotary evaporator (Laborata 4000; Heidolph Instruments GmbH & Co. KG; Germany). A sample of the extract was analyzed for phytocannabinoid composition using a Thermo Scientific ultrahigh-performance liquid chromatography (UHPLC) system coupled with a Q Exactive Focus Hybrid Quadrupole-Orbitrap MS (Thermo Scientific, Bremen, Germany). The chromatographic method and MS parameters are detailed in Phytocannabinoid Analysis Method 1 (see Methods in the Supporting Information). Identification and absolute quantification of phytocannabinoids was performed by external calibrations as described by Berman et al.5
2.3Microdepot Preparation
Microdepots encapsulating whole-plant Cannabis extract were prepared via a melt printing technique.33 Briefly, molten PCL was mixed with 30 wt % CBD-rich extract at 60 °C. Then, the mixture was jetted through a 100 μm flat nozzle onto nonwetting surfaces using a pneumatic jetting apparatus (P-Dot CT, Liquidyn [Nordson EFD], Oberhaching, Germany). A fluid temperature of 90 °C, fluid pressure of 0.1 bar, valve pressure of 4.9–5.1 bar, spring tightness of 0.6 turns and distance of ∼10 mm between the nozzle and the surface were applied to form discrete microspheres. The microdepots were left to cool to room temperature and stored at −4 °C until further use. The formation of the microdepots was captured using a digital high-speed camera (120 Phantom v12) equipped with a microscopic lens (Nikon 10 x CFI Plan Achromat), at a frame rate of 48 000–58 000 fps.
2.4Microdepot Characterization
The particle size and size distribution of the microdepots were determined using a Malvern Mastersizer 3000 laser diffraction particle sizer (with a Hydro EV unit). The surface morphology of the microdepots was observed using a scanning electron microscopy. The microdepots were sputter-coated with Au–Pd alloy and then imaged using a JEOL JSM-IT200 SEM operated at an acceleration voltage of 20 kV. The appearance of the microdepots was imaged using a Dino-Lite Premier AM7013MZT digital hand-held microscope.
2.5Phytocannabinoid Encapsulation Efficiency
Cannabis extract microdepots (approximately 3 mg) were dissolved in 200 μL of dichloromethane, then precipitated with 4 mL ethanol followed by vortex for 1 h. The suspension was filtered through 0.22 μm PTFE-filters to remove polymeric debris and, analyzed for phytocannabinoid concentration with a Thermo Scientific UHPLC system coupled with an ISQ EC Single Quadrupole MS (Thermo Scientific, Bremen, Germany) as described in Phytocannabinoid Analysis Method 2 (see Methods in the Supporting Information). Phytocannabinoid encapsulation efficiencies were determined by dividing the measured phytocannabinoid content by the theoretical value. Only phytocannabinoids constituting more than 0.5 wt % of the extract were reported.
2.6Thermal Stability
To examine the long-term thermal stability of the Cannabis extract at the processing temperature, we kept the molten mixture at 90 °C and sampled at 1, 10, 20, and 30 h time points. The samples were prepared and analyzed by LC/MS as described in the former section to determine phytocannabinoids content.
2.7In Vitro Release Study
In vitro release kinetics of phytocannabinoids from the polymeric microdepots was determined by incubation in PBS under sink conditions. Microdepots weighing approximately 6 mg were suspended in 20 mL PBS (pH 7.4) containing 0.1% w/v Tween 20 at 37 °C under constant agitation. At predetermined time intervals, the release medium was withdrawn and replenished with fresh prewarmed medium. The obtained supernatant was freeze-dried, dissolved in 1 mL of ethanol, filtered, and then analyzed for phytocannabinoid content by LC/MS (see Phytocannabinoid Analysis Method 2 in Methods in the Supporting Information). SEM analyses were employed as previously described, to determine changes in microdepot sizes and surface morphologies during the dissolution test, and optical images were taken to follow their appearance.
2.8In Vivo Release Study and Pharmacokinetics
The in vivo release characteristics of the microdepots were studied in mice. Animal studies were performed in compliance with the Guide for the Care and Use of Laboratory Animals established by the National Institutes of Health. All procedures and protocols were approved by the Technion Administrative Panel of Laboratory Animal Care (#:IL_050–05–2018). Adult male mice weighing 20–25 g (C57BL/6 J; The Jackson Laboratory) were randomly assigned to two groups and treated with either Cannabis extract microdepots or a Cannabis extract solution. Samples of Cannabis extract microdepots were suspended in 1 mL injection medium containing 1% w/w carboxymethylcellulose and 1% w/w Tween20 in saline.34 The suspended microdepots were then administrated via subcutaneous injection through a 20g syringe into mice at a dose of 200 mg/kg extract under isoflurane anesthesia. As a control, Cannabis extract dissolved in 1:1:18 ethanol:cremophor:injection medium (25 mg/mL), was injected subcutaneously at an equivalent dose. Four mice from each group were sacrificed at 1, 2, 3, 7, and 14 days postadministration, and blood samples were collected via cardiac puncture. Blood samples were set aside for 30 min at room temperature and then centrifuged for 30 min at 4 °C. Serum was collected and stored at −80 °C until analysis. Area under curve (AUC) values were calculated directly from the serum concentration–time curve using the linear trapezoidal method, from the first day to the last time point.
Phytocannabinoid extraction from serum was performed as follows: 600 μL of the extraction solution (0.1% v/v acetic acid in a methanol:acetonitrile 1:1 mixture) spiked with 20 ng/mL deuterated internal standards (ISs) were added to 200 μL of serum samples. Samples were thoroughly vortexed and then centrifuged for 20 min at 4 °C for protein and cell precipitation. The supernatants were then transferred into 3 mL of 0.1% v/v acetic acid in water, and loaded onto Agela Cleanert C8 solid phase extraction (SPE) cartridges (500 mg of sorbent, 50 μm particle size). Phytocannabinoids were eluted from the columns using 2 mL of 0.1% v/v acetic acid in methanol, evaporated to dryness by speedvac, and reconstituted in 100 μL of ethanol. Phytocannabinoids in serum samples were analyzed using a Thermo Scientific UHPLC system coupled with a Q Exactive Focus Hybrid Quadrupole-Orbitrap MS (Thermo Scientific, Bremen, Germany).5 The chromatographic and mass spectrometric parameters were the same as those described in Phytocannabinoid Analysis Method 1 (see Methods in the Supporting Information). For quantification of phytocannabinoids in serum samples, phytocannabinoid standards were prepared in ethanol to concentrations ranging from 0.2 to 2000 ng/mL for Δ9-THCA, Δ9-THC, CBDA, and CBD, and 0.125 to 500 ng/mL for all the other components. Standard calibration curves were then constructed by adding similar volumes of each concentration standard and a mixture of all deuterated ISs at a concentration of 30 ng/mL. The ratios of the unlabeled and labeled ions were plotted against the amounts of spiked standards, and the calibration curves were determined empirically according to a weighted least-squares linear regression method with a weighting factor of 1/X.
At the same time points, the microdepots were collected from the injection site, washed with ddH2O to remove cellular debris, and freeze-dried. Samples of dried microdepots (approximately 3 mg) were then dissolved in dichloromethane and prepared for LC/MS analysis as described in the Encapsulation Efficiency section to determine the remaining phytocannabinoid content. In addition, the morphology and appearance of the microdepots after release were documented.
2.9Microdepot Anticonvulsant Activity
The anticonvulsant activity assay was based on previous work.5 One week following administration of Cannabis extract microdepots or Cannabis extract solution (as described above), mice (n = 10) were subcutaneously injected with PTZ by a treatment-blind experimenter at a dose of 80 mg/kg and then monitored for 30 min. The epileptic seizures were captured using a video recording system for epileptic seizures analysis in real-time (SeizureScan, Clever Sys., Inc., Virginia, USA), and the progress of seizure activity from normal behavior (P0) to behavior arrest (P1), to twitches (P2), to forelimb clonus (P3), to generalized clonic convulsions (P4), to tonic-clonic convulsions (P5) was recorded. The latency to first P5 convulsions, incidence of P5 convulsing animals and survival were analyzed. Following this monitoring, blood samples were collected from surviving mice via cardiac puncture to determine phytocannabinoid serum levels.
2.10Statistical Analysis
In the microdepots characterization and release studies, data were determined as mean ± SD. In the study of microdepot anticonvulsant activity, the latency to first tonic-clonic seizures was determined as mean ± SEM. Significant differences in latency between experimental groups were determined using a paired student t test with p value <0.05. Percent of protection against development of tonic-clonic seizure and death subsequent to PTZ administration was compared using the χ2 test with p value >0.05 for both seizure protection and mortality protection.
3Results
3.1Formation and Characterization of Cannabis-Loaded Microdepots
The phytocannabinoid profile of the decarboxylated high-CBD Cannabis extract used in this study appears in Table 1. The extract contained more than 50 wt % CBD and five other phytocannabinoids, CBDA, CBG, Δ9-THC, CBC, and CBDV, having a weight percent above 0.5%. After mixing the liquid extract with the molten PCL, a solid mixture was obtained upon cooling, entrapping 30 wt % of the whole extract. A melt printing technique33,35 was employed to produce polymeric microdepots. The deposition of the molten mixture on top of nonwetting surfaces using a pneumatic jetting apparatus operating at temperatures above the melting point of the polymeric system, yielded discrete, near-perfect spherical microparticles. Figure 1A shows a sequence of images captured using a high-speed camera emphasizing the spontaneous formation of an extract-loaded microsphere, upon interaction of the molten jet with the oleophobic substrate (the captured video can be seen in Video S1). The microspheres preserve their spherical shape during solidification and appear brown in color (Figure 1B). Scanning electron microscopy (SEM) images revealed round, uniform, and individualized microparticles, with a textured surface (Figure 1C), distinct from the smooth surface obtained for neat PCL microspheres printed from melt.35 The particle size distribution was narrow and monodispersed, with a d50 of 257.80 ± 2.49 μm and a span value of 0.68 ± 0.05 μm, as measured using laser diffraction analysis (Figure S1).
| phytocannabinoid | content (wt %) | EE (%) |
|---|---|---|
| CBD | 54.68 | 102.5 ± 0.6 |
| CBDA | 2.50 | 92.1 ± 1.2 |
| Δ9-THC | 2.36 | 103.5 ± 2.4 |
| CBG | 2.35 | 90.0 ± 4.1 |
| CBC | 2.17 | 93.5 ± 2.1 |
| CBDV | 1.65 | 101.1 ± 3.7 |
| CBDVA | 0.42 | |
| CBN | 0.20 | |
| Δ9-THCV | 0.17 | |
| CBGA | 0.09 |
Recent developments in the field of micro- or nanoparticles for controlled phytocannabinoid delivery involve only single constituents, such as CBD,27,31,32 Δ9-THC,28,31 and CB13.26,30,36 None have described the encapsulation of the full spectrum of Cannabis phytocannabinoids. Here, we were able to encapsulate all the phytocannabinoids present in the extract above 0.5 wt %, with encapsulation efficiencies of more than 90% (Table 1). This high encapsulation efficiency is possibly due to the closed environment of the melt processing and the exclusion of organic solvents.33,37 However, one potential concern with melt processing techniques involves the exposure of active pharmaceutical ingredients to elevated temperatures.38,39 Considering phytocannabinoid susceptibility to heat degradation,40 the thermal stability of the phytocannabinoids in the polymeric matrix was studied during and postprocessing. Figure S2 shows that phytocannabinoid compositions remained nearly constant during microdepot printing and within the first 10 h. Afterward, a decrease in CBDA, CBD, and Δ9-THC contents and an increase in cannabinol (CBN) content were detected, possibly due to decarboxylation of the acidic phytocannabinoids to their neutral forms and oxidation reactions.15,41,42
3.2In Vitro Phytocannabinoids Release
Prior to the in vivo study, we evaluated the feasibility of the polymeric carrier to sustain phytocannabinoids release in vitro, under simulated physiological conditions. Figure 2A presents the in vitro release profiles, over 21 days, of the different phytocannabinoids in the extract-loaded microdepots. The microdepots showed a sustained release profile, in total releasing 70% of the entrapped predominant phytocannabinoid, CBD, and 52–64% CBDV, CBG, Δ9-THC, and CBC with no initial burst release. CBDA, the acidic precursor of CBD, was released much faster than the other neutral phytocannabinoids, accounting for 70% cumulative release after 1 day, probably because of its higher aqueous solubility that increased the molecule propensity for diffusion.43 The slightly lower cumulative release amounts of CBDV, CBG, Δ9-THC, and CBC compared to CBD may be related to the lower loadings of these minor phytocannabinoids.44 The micrographs of the microdepots taken during the dissolution study (Figure 2B–E) revealed no significant changes in microdepot sizes or evidence for surface erosion. Magnified micrographs (Figure 2F–I) show the formation of pores in the microdepots’ surface that grew over time from hundreds of nanometers to several micrometers. Pristine PCL microdepots incubated in the same release medium remained intact during the study period, as can be seen in Figure S3. These findings, along with PCL’s inherent semicrystalline, low vitreous transition temperature, and hydrophobic nature, suggest that diffusion is the governing mechanism of the Cannabis components’ release from the polymeric carrier.27,45,46
3.3In Vivo Phytocannabinoid Release
Biodegradable polymeric microdepots are widely used to deliver medications in a rate-controlled manner.47 However, direct analysis of these systems during release studies in vivo is rarely reported. The performance of the formulation within the subcutaneous tissue is usually predicted based on in vitro dissolution tests followed by deconvolution of pharmacokinetic data to estimate the in vivo absorption profile.48,49 These predictions are rarely accurate, because current in vitro environments do not accurately reflect the biological factors present in the subcutaneous environment, that largely affect the drug release kinetics.50−52 Therefore, to evaluate the in vivo performance of the formulation, mice were injected with a single subcutaneous injection of Cannabis-loaded microdepots, or a Cannabis extract solution at an equivalent dose. At different time points, microdepots were collected from the subcutaneous tissue in order to evaluate the amounts of phytocannabinoids released, and phytocannabinoids’ serum levels were analyzed to obtain pharmacokinetic profiles.
Because the microdepots did not migrate from the injection site, we were able to recover them (Figure S4) and directly analyze the release behavior in vivo. Phytocannabinoid release profiles were determined according to their remaining content in the retrieved microdepots. CBDA was not detectable in the recovered microdepots 24 h post administration, in correlation with its fast release in vitro. Figure 3A demonstrates sustained phytocannabinoid delivery, with close to zero-order release kinetics during the first week (R2> 0.980 in linear regression), followed by a slower release rate during the second week, corresponding to the deceleration in the release rate in vitro after the first week. An empirical model correlating between the phytocannabinoids in vivo release rate within the first week (zero order release rate) and their physiochemical characteristics was examined. As can be seen in Figure 3B, a linear relationship (correlation coefficient of 0.985) between phytocannabinoids’ average release rate, lipophilicity (Log P) and molecular weight (Mw) was found, following the expression:Log P values (logarithm of partition coefficient) were calculated using ChemAxon software. The model depicts that the greater the lipophilicity of a phytocannabinoid, the faster it releases, possibly because of the lipophilic nature of the subcutaneous site. In contrast, the larger the molecules are, the slower they diffuse. This relationship may then be applied to predict the in vivo release behavior of other phytocannabinoids, which might be included in other Cannabis strains.
The microstructure of the recovered microdepots was also investigated at different stages of the release study and no signs of surface erosion or deformation were observed (Figure 3C–F). The pores that were formed on the microdepots’ surface reached dimensions of several microns after 1 week (Figure 3G–J), faster than in the dissolution study, corroborating with the observed higher released amounts (Figure 3A). In addition, the appearance of the microdepots was documented during the in vitro and in vivo release studies. As shown in Figure 4, the microdepots gradually lost their brown color with time. This might be the result of sustained release from the polymer matrix of other pigment molecules usually present in Cannabis extracts, such as flavonoids, carotenoids, and chlorophylls.7
Serum levels of 3 predominant neutral phytocannabinoids, CBD, Δ9-THC, and CBG were measured, and their pharmacokinetic profiles are shown in Figure 5. Because the first blood samples were taken 24 h postdose, phytocannabinoid levels at shorter times were not available. Administration of Cannabis extract solution for immediate release resulted in a more abrupt increase in phytocannabinoid bloodstream levels and faster elimination compared to microdepots administration. Importantly, microdepot administration resulted in sustained, elevated serum phytocannabinoid levels, over the 14 day study period. The serum concentration of CBD reached a maximum during the first day following injection, then decreased gradually and was maintained at a steady level, significantly higher than the immediate-release group (p < 0.05). To determine the relative bioavailability, we compared the AUC1–14 from microdepot administration to the AUC1–14 from solution administration of Cannabis extract. Over the 14 day time period, the relative bioavailability of the CBD released from the extract in microdepots was more than two-fold higher than that of the extract solution. Significantly higher steady serum levels (p < 0.05), enhanced bioavailability and extended absorption duration were observed also for CBG and Δ9-THC, despite their much lower content. This demonstrates the potential of the formulation to improve the systemic exposure of both major and minor components, which is important for supporting potentially synergistic effects. It should be noted that the microdepots and the immediate-release extract were suspended in the same injection medium for administration, in order to control for the effects of the medium on the delivery of the therapeutic agents into the bloodstream.
3.4Microdepot Anticonvulsant Activity
The therapeutic potential of the microdepots as a controlled release formulation for whole-plant Cannabis extracts was evaluated via a PTZ model in mice. The specific Cannabis extract used was chosen after it has previously demonstrated superior anticonvulsant effects when compared to different equally high-CBD Cannabis strains against PTZ-induced convulsions, 30 min post Cannabis injections, when phytocannabinoid circulation levels were high.5 Here, in order to evaluate the long-term activity of the microdepots, we administered PTZ injections to mice 1 week after a single subcutaneous injection of Cannabis-loaded microdepots or Cannabis extract solution. Mice were monitored for 30 min after induction, and the epileptic seizures were analyzed and ranked according to a seizure profile. The microdepots showed greater reduction in the incidence of tonic-clonic seizures, higher survival rates and increased latency to first tonic-clonic seizure, compared to the extract solution injected control group (Figure 6A, B). In addition, the phytocannabinoid levels measured at day 7 (Figure 6C) were similar to those obtained in the in vivo release study at the same time point, indicating the reproducible release of the active agents from the polymeric microdepots.
4Discussion
In this study, we have proposed a novel Cannabis delivery system, in the form of polymeric microdepots, for full-spectrum Cannabis administration. Encapsulating Cannabis extract in a PCL matrix via a one-step printing process was effective in entrapping a wide range of phytocannabinoids in a single polymeric microdepots and modulating their release rate. Similar sustained release of both major and minor phytocannabinoid components was observed and this important for supporting potential synergistic effects of multiple components. Cumulatively higher phytocannabinoid amounts were released from the microdepots in vivo by day 14 and with greater variance between the different phytocannabinoids, compared to the in vitro release study. Although only limited information is currently available regarding the in vivo release of pharmaceuticals from PCL, it can be assumed that the faster release kinetics in vivo are a result of an accelerated diffusion rate due to the presence of biological compounds such as lipids.53,54 These biological factors, which are not accurately represented in vitro, probably contributed to the observed difference in phytocannabinoids’ transport rate at the subcutaneous site, as had been shown in the empirical model. This model provided insights into the release and delivery kinetics of several active ingredients in vivo as a function of their physiochemical properties. These findings may contribute to the future development of “polypills” in which multiple active pharmaceutical ingredients are incorporated in a single dosage form.55 The sustained release enhanced the bioavailability and elevated phytocannabinoid levels in the serum up to 14 days following administration, significantly increasing the in vivo residence time of these highly lipophilic molecules. Moreover, the growing evidence for high-CBD extract’s efficacy in treating seizure disorders14,56 had led us to evaluate the potential of the depots to promote long-term anticonvulsive activity using the PTZ seizure model. PTZ has been previously shown to be a useful model for evaluating cannabinoids anticonvulsant effects in murines.57−59 The depot’s effectiveness against PTZ-induced convulsions was demonstrated 1 week after subcutaneous administration, compared to a bolus of pure Cannabis extract. This implies that long-acting microdepots are suitable for the parenteral delivery of medicinal Cannabis and might prolong its therapeutic action while attenuating peak serum levels, significantly differing from the current conventional Cannabis treatment for epilepsy, based on a twice daily oral dose administration.60,61 Such systems may provide a convenient and stable long-term treatment for patients suffering from chronic conditions or may supply an alternative delivery form for those incapable of inhaling or swallowing.
5Conclusions
Existing implantable drug delivery depots are designed to release only a single phytocannabinoid, even though it is suggested that whole-plant Cannabis extracts have superior therapeutic effects over individual components. Herein, we propose the use of long-acting polymeric microspheres, performing as depots, for the encapsulation and controlled delivery of the full Cannabis plant spectrum. In mouse models, we demonstrate that these depots are capable of simultaneously delivering multiple phytocannabinoids and significantly extending their circulation time. Therefore, these depots may be advantageous for harnessing long-term Cannabis therapeutic potential while supporting potential synergistic interactions between the plant’s components, as demonstrated in an acute convulsion model.
Supporting Information Available
The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsami.0c04435.
- Phytocannabinoid analysis method 1, phytocannabinoid analysis method 2, particle size analysis of Cannabis extract microdepots, effect of printing temperature on phytocannabinoids content in the polymer matrix, SEM micrographs of blank PCL microdepots, Cannabis extract microdepot removal from mice (PDF)
- Video S1, formation of a Cannabis-loaded microdepot upon interaction of the molten jet with the nonwetting surface (MP4)
Supplementary Material
Notes
The authors declare no competing financial interest.
Acknowledgments
This work was supported by the Israeli Ministry of Economy Innovation Authority (Grant 63294). We thank the Evelyn Gruss Lipper Charitable Foundation and the Israeli Ministry of Agriculture and Rural Development, for their financial support for some parts of this work. The authors thank Dr. Nir Debotton for assistance with the laser diffraction analysis; Mr. Ohad Guberman for the extraction and sample preparation of the Cannabis strains; and Canndoc company for providing the Cannabis inflorescences on which this study was based.