TiO2 Films Modified with Au Nanoclusters as Self-Cleaning Surfaces under Visible Light
Laboratory of Solid-State Physics and Magnetism, KU Leuven, Celestijnenlaan 200D, Box 2414, BE-3001 Leuven, Belgium; tingwei.liao@kuleuven.be (T.-W.L.); anupam.yadav@kuleuven.be (A.Y.); didier.grandjean@kuleuven.be (D.G.); peter.lievens@kuleuven.be (P.L.)
Sustainable Energy, Air & Water Technology (DuEL), University of Antwerp, Groenenborgerlaan 171, BE-2020 Antwerp, Belgium
Center for Surface Chemistry and Catalysis, KU Leuven, Celestijnenlaan 200F, BE-3001 Leuven, Belgium
Electron Microscopy for Materials Research (EMAT), University of Antwerp, Groenenborgerlaan 171, BE-2020 Antwerp, Belgium; nathalie.claes@uantwerpen.be (N.C.); sara.bals@uantwerpen.be (S.B.)
Abstract
In this study, we applied cluster beam deposition (CBD) as a new approach for fabricating efficient plasmon-based photocatalytic materials. Au nanoclusters (AuNCs) produced in the gas phase were deposited on TiO2 P25-coated silicon wafers with coverage ranging from 2 to 8 atomic monolayer (ML) equivalents. Scanning Electron Microscopy (SEM) images of the AuNCs modified TiO2 P25 films show that the surface is uniformly covered by the AuNCs that remain isolated at low coverage (2 ML, 4 ML) and aggregate at higher coverage (8 ML). A clear relationship between AuNCs coverage and photocatalytic activity towards stearic acid photo-oxidation was measured, both under ultraviolet and green light illumination. TiO2 P25 covered with 4 ML AuNCs showed the best stearic acid photo-oxidation performance under green light illumination (Formal Quantum Efficiency 1.6 × 10−6 over a period of 93 h). These results demonstrate the large potential of gas-phase AuNCs beam deposition technology for the fabrication of visible light active plasmonic photocatalysts.
Untitled section
Keywords: photocatalysis, gold nanoclusters, plasmonics, cluster beam deposition, stearic acid, self-cleaning surfaces
Article notes
Untitled section
Received 2017 Nov 14; Accepted 2017 Dec 28; Collection date 2018 Jan.
1. Introduction
Various semiconductor-based photocatalysts, such as TiO2, ZnO, SrTiO3, Fe2O3, FeOOH, WO3, CdS and III–V compound semiconductors, have drawn considerable attention in recent years [1,2,3,4,5,6,7,8,9,10,11,12], due to their multiple promising applications in solar energy harvesting [13,14,15], water cleaning [16,17,18], anti-bacterial surfaces [19], organic pollutants removal [20] and self-cleaning surfaces [21] as new construction materials for the improvement of the urban environment. The main factors that determine the photocatalytic properties of semiconductor-based photocatalysts are band gap, position of conduction band and valence band, mobility of photo-generated charge carriers and material stability [22]. Although titanium dioxide (TiO2) is a good photocatalyst towards oxidation of organic compounds under ultraviolet (UV) light [23], its photocatalytic properties need to be improved significantly in the visible range, especially under green light that corresponds to the maximum output range of the sun’s total irradiance spectrum. Surface modification with metal nanoparticles improves the photoabsorption rate in the visible range by (amongst other phenomena) hot electron injection effects produced by their localized surface plasmon resonance (LSPR) [24,25,26].
Most of the metal nanoparticle-TiO2 composites nowadays are synthesized in solution by various wet chemistry synthesis protocols that generally include inorganic acid in the particle synthesis, toxic ligands to protect the metal particles and functional groups that stabilize the nanoparticles (NPs) on the TiO2 surface [14,27,28]. It has been shown that the performance of the NPs is highly affected by the chemical environment during the preparation processes. Therefore, the use of acids and ligands in wet chemistry synthesis methods can have a significant inference on the NPs [29]. Furthermore, by ensuring the NPs are only present at the surface can reduce the usage of the amount of noble metals. Cluster beam deposition (CBD) greatly benefits from producing clusters in a well-controlled noble gas environment and then soft landing them on supports while maintaining their preformed structure with excellent control over size, shape, and composition [30]. In order to produce clean and controllable photocatalytic systems with only desired materials, physical cluster beam deposition methods that produce size-selective nanoclusters or nanoparticles (NCs/NPs) in noble gas environments, free of unwanted ligands or functional groups, present a very attractive alternative.
In this study, we report on the significant improvement of the photocatalytic activity of TiO2 P25 films modified with AuNCs produced by the laser ablation cluster beam deposition technology, with equivalent coverage ranging from 0 ML to 8 ML (1 ML ~1.5 × 1015 atoms/cm², ~0.5 μg/cm²) towards stearic acid degradation under UV (365 nm) and green LED light (515 nm) irradiation. The photocatalytic efficiency of AuNCs modified TiO2 films with an equivalent cluster coverage of 4 ML was enhanced by a factor of 4 compared to pristine TiO2 P25 under green LED irradiation while no significant effect of AuNCs on the activity was noticed under UV exposure.
2. Results
2.1. Morphology of Au Nanoclusters Modified Films
Figure 1a shows a Scanning Electron Microscopy (SEM) image of the TiO2 P25 film, supported on a Si wafer. TiO2 P25 films are uniform and no apparent regions or island discontinuities are observed on the sample surface at this scale. SEM images of 2 ML, 4 ML and 8 ML of AuNCs modified TiO2 P25 films are presented in Figure 1b–d, respectively. Due to the lower ionization potential of Au compared to TiO2, the electron intensity from AuNCs is higher allowing AuNCs to be revealed. The cluster size is determined by the cluster projected area and the cluster size distributions are presented in Figure 1e (2 ML), Figure 1f (4 ML) and Figure 1g (8 ML). All the coated TiO2 P25 films are homogeneously covered by AuNCs. At the lowest coverage (2 ML) most of AuNCs have an average size of 5.2 nm and appear individually without any sign of aggregation while at the highest coverage (8 ML) AuNCs with a larger size of 7.8 nm and irregular shapes are observed suggesting a significant level of cluster coalescence. The morphology of the 4 ML sample consists mainly of individual clusters with an average size of 5.5 nm very similar to the NCs in the 2 ML sample. The mobility of the Au atoms on TiO2 has been studied by Scanning Tunneling Microscopy (STM) and the binding energy of Au atoms on TiO2 was investigated by Density Functional Theory (DFT). Both of these studies show that the binding energy of Au atoms and clusters is low enough so that Au clusters can become mobile on the TiO2 surface [31,32]. Therefore, when the coverage of Au clusters increases, the chance of Au clusters to coalesce will increase and result in larger and irregularly shaped particles.
Optical characterization of the AuNCs revealed that for all three modified samples, a typical gold surface plasmon resonance (SPR) band is observed at a wavelength of ca. 520 nm, as expected for small gold clusters (Figure 2). The absorbance intensity of the SPR band increases as the gold loading on the sample increases. It is also striking that the absorption onset for the 8 ML sample is strongly red-shifted compared to the other samples and the SPR band is broadened. This is in full agreement with the larger average particle size, degree of coalescence and irregular shape of the particles observed by SEM for this particular sample.
2.2. Photocatalysis on Stearic Acid
The integrated area of the Fourier-transform infrared (FTIR) absorbance spectra between 2800 and 3000 cm−1 as a function of time with different coverage is shown in Figure 3a,b for stearic acid degradation under UV and green LED light, respectively. The quantity of stearic acid remaining on the sample surface decreased linearly with time, indicating a zero order degradation kinetics. This is consistent with the self-cleaning behavior of plasmonic photocatalysts reported in earlier work [24]. A series of blank reference experiments was done in our previous work to exclude the possible contributions of photolysis, plasmonic heating or direct plasmonic catalysis on the noble metal clusters by investigating a blanc silicon wafer and samples with direct deposition of noble metal clusters but without TiO2. The results showed that these samples present no activity under either UV, 490 nm LED light, nor simulated solar light [24].
In Figure 3 red lines correspond to the TiO2 P25 films without Au cluster modification while the orange, yellow and the green lines to TiO2 P25 films modified with 2 ML, 4 ML, and 8 ML of AuNCs, respectively. The photocatalytic activities of TiO2 P25 under UV towards stearic acid degradation were not improved upon modification with AuNCs. The activity was even disrupted to some extent at the highest coverage of 8 ML. Under green LED light illumination, however, all the photocatalytic activities of AuNCs modified TiO2 films were enhanced significantly. These results are preferably expressed as “Formal Quantum Efficiency” (FQE) for comparison [33], which is defined as
The FQE under UV and green light illumination as a function of Au coverage are presented in Figure 4a,b, respectively.
Under UV illumination, the performance of all samples is similar. The FQE of the pristine TiO2 P25 reference film under UV was measured to be 3.7 × 10−3. The value measured by Mills et al. was 4.8 × 10−3 for the same type of catalyst, which is in very good agreement with our result given the fact that their film was prepared with a three-time dipping-drying process that leaves a larger amount of catalyst on the film [33]. This result is also in line with the findings of Allain et al. for a mesoporous TiO2 film (1.02 × 10−3) [34]. Our results show that modification with noble metal NCs did not improve the activity of the pristine reference sample under UV irradiation nor disrupt it until an equivalent Au coverage of 8 ML is reached. For the latter 8 ML sample a 20% decrease in degradation efficiency is observed under UV illumination. This may be attributed to an incremental blocking of the catalyst active sites, or to the fact that a larger fraction of incoming light is prevented from reaching the catalyst in comparison to the samples featuring lower Au coverages.
Under pure green visible LED light, a very clear positive effect in the presence of metallic AuNCs for all the samples is observed. This is ascribed to the plasmonic effect of AuNCs, active in this wavelength range. At first, it should be noted that the pristine TiO2 P25 features a small photocatalytic activity under green LED light illumination, which is rather unexpected and controversial. In principle visible light cannot initiate photocatalytic reactions on a TiO2 surface, as its photon energy is much lower than the TiO2 P25 band gap of 3.1 eV [35]. A possible explanation could be related to the presence of defect states present in the band gap of TiO2 P25 that enable the generation of charge carriers in pristine TiO2 P25 upon pure visible light excitation as has been demonstrated by means of Electron Paramagnetic Resonance (EPR) measurements [36]. This low basal activity under visible light was also observed in our previous study and could not be attributed to thermal degradation nor to pure photolysis processes [24].
3. Discussion
Upon modification of TiO2 with AuNCs, a significant increase of the photocatalytic efficiency under 515 nm green light is observed for all coverages. Although a modest increment is found for 2 ML AuNCs modified TiO2 P25 films, a FQE 4 times greater than the reference and 2.5 times greater than the 2 ML sample was measured in the 4 ML sample. However, further doubling the AuNC coverage to an equivalent of 8 ML resulted in a lowered efficiency, which may again be explained by an excessive blocking of the active sites and/or by unwanted light scattering. The hypothesis is supported by the observation of the SEM images. The size of the NCs at the surface of the 8 ML sample is larger compared to the other lower coverages, which is suggesting cluster aggregation and coalescence happened on the sample surface. This is also confirmed by broadening of the UV-Vis absorption spectrum of the clusters. Furthermore, the surface of the TiO2 P25 powder film is almost fully covered by AuNCs. The photocatalytic activity of pure noble metal clusters was studied in previous work and it was shown there is no photocatalytic nor photo-thermal activity of noble metal nanoparticles as such [24]. It was also studied that the active site is located at the metal-support site. The availability of both metal and support are necessary for the reaction to occur. Therefore, as the AuNCs coverage increases on the TiO2 surface, the accessibility of the AuNCs-TiO2 site reduces [37]. As a combined result of these effects, the photocatalytic activity of 8 ML Au cluster modified TiO2 P25 film is reduced.
AuNCs feature a strong light absorption in the visible region where the absorbed energy can induce resonant oscillation of the free electrons present in the Au clusters [38]. The trapped energy can then be transferred to the coupled semiconductor substrate by a variety of mechanisms [39]. This was highlighted by electron paramagnetic resonance (EPR) studies of Au-TiO2 composites that showed that hot electron transfer from a gold excited plasmonic state into the TiO2 conduction band is an important underlying mechanism (Figure 5) [38,40].
One of the other advantages of the gas phase Au cluster deposition method, is that the active particles are exclusively located at the surface of the powder film where they can efficiently interact with incident photons, and not in the bulk. This increases the efficiency of material usage. For instance, the weight per area of 4 ML AuNCs is estimated to be only 2 μg/cm².
Although the IUPAC recommends to express the photocatalytic activity in terms of FQE, there is not yet a standard way to present the photocatalytic activity in the photocatalysis community. Therefore, it is difficult to compare the photocatalytic activity of our system to recent literature results. The 4 ML AuNCs film demonstrates higher photocatalytic activity compared to our previous studies on Au-Ag bimetallic plasmonic particles. It was found that TiO2 P90 (90% anatase, 10% rutile) modified with 1.5 wt % of Au0.3Ag0.7 plasmonic alloy nanoparticles under 490 nm teal light illumination resulted in a FQE of 0.39 × 10−6 [25]. In the present work, the FQE of 4 ML AuNCs modified TiO2 P25 under 515 nm green light is 1.7 × 10−6. In another study AuxAg1−x (x = 0.2 to 1) nanoparticles were deposited on TiO2 P25, resulting in a so-called rainbow photocatalyst that was 16% more effective than pristine TiO2 P25 under both simulated and real solar light toward stearic acid degradation (i.e., combined UV and visible light irradiation) [24]. The excellent photocatalytic activity enhancement observed under green light obtained with pure AuNCs in this study suggests that fabricating a similar “rainbow” photocatalyst using our physical gas phase cluster deposition method may lead to further enhancements of the photocatalytic activity, and is the subject of ongoing research.
4. Materials and Methods
4.1. Preparation of Au Nanoclusters Modified Films
TiO2 P25 powder (Evonik, Hanau-Wolfgang, Germany, 70% of anatase and 30% of rutile) films were prepared by spin coating 1 wt % of titania powder ethanol suspension at 1500 rpm onto low-doped Si wafers with 3 cm in length and 1.5 cm in width followed by subsequent overnight drying at 70 °C. Next, TiO2 P25 powder films were modified with AuNCs with equivalent atomic coverages of 0 ML, 2 ML, 4 ML and 8 ML by depositing gas phase AuNCs produced with a laser ablation cluster source. Clusters are produced by pulsed laser (10 Hz, Nd:YAG lasers, Spectra Physics, Santa Clara, CA, USA, INDI) ablation of Au (ACI Alloy, San Jose, CA, USA, purity 99.995%) plate targets and condensation in a high pressure (9 bar) of inert gas (He, purity 99.9999%) [41]. The cluster source was cooled by liquid nitrogen, resulting in a NC temperature of about 100 K. In this study, the cluster size distribution was optimized for sizes in the order of 1000 atoms. Following a supersonic expansion into vacuum of the helium carried NC molecular beam, AuNCs were soft-landed (~500 m/s) on the P25 films in a ultra-high vacuum (UHV) cluster deposition chamber under a base pressure below 5 × 10−10 mbar [18]. The cluster flux was monitored by a quartz crystal microbalance (QCM) and the cluster coverage controlled by the deposition time under a fixed cluster flux.
4.2. Film Characterization
Secondary electron SEM images of TiO2 P25 films and AuNCs modified P25 films were acquired using a FEI Quanta 250 FEG environmental scanning electron microscope (Thermo Fisher Scientific—FEI, Hillsboro, OR, USA). The microscope was operated at 15 kV with a chamber pressure of 130 Pa. UV-Vis absorption spectra of the AuNCs were collected as-deposited on the films using a double beam UV2600 spectrophotometer (Shimadzu, Kyoto, Japan) equipped with film holders attached to a BaSO4 coated integrating sphere of 60 mm in diameter. A pristine TiO2 P25 film was used as the background sample.
4.3. Photocatalysis towards Stearic Acid Degradation
AuNCs modified films were then spin coated with 100 μL of a 0.25 wt % stearic acid solution in chloroform at 1000 rpm for 1 min and the stearic acid coated films dried in an oven at 70 °C for 15 min. Finally the samples were exposed to the ambient overnight to establish a thermal and humidity equilibrium before the photocatalytic measurements. The photocatalytic activity tests were performed at ambient conditions at a temperature of 32 ± 2 °C and a relative humidity of 34 ± 3% (monitored with a Humidity and Temperature Transmitter (Vaisala, Helsinki, Finland)) under UV and green light irradiation. The photon flux of UV and green light LED lamp emission were 2.9 × 1015 photons/cm2/s in 300 nm to 400 nm spectral range and 8.1 × 1015 photons/cm2/s in 450 nm to 600 nm spectral range, respectively, as measured with an Avantes Avaspec Spectroradiometer (Avantes BV, Apeldoorn, The Netherlands).
The degradation of stearic acid during illumination was measured by recording FTIR absorbance spectra (Thermo Nicolet 6700, Thermo Fisher Scientific, Madison, WI, USA) with 1 cm−1 resolution of the solid film placed at a fixed angle of 9° with the IR beam in order to minimize internal reflection effects. The quantity of stearic acid remaining on the sample surface was determined by integrating the area of the IR band between 2800 and 3000 cm−1, which consists of the asymmetric νas (–CH3) vibration at 2958 cm−1, the asymmetric νas (–CH2) at 2923 cm−1 and the symmetric νs (–CH2) at 2853 cm−1 of the stearic acid hydro-carbon chain, and the results were plotted versus illumination time. The degradation experiments under UV illumination were performed over 15 min and the experiments under green light were monitored over a period of 93 h. This methodology was validated in earlier work of various authors [25,33,42].
5. Conclusions
We have demonstrated the excellent photocatalytic self-cleaning activity of a series of TiO2 P25 films modified with gas phase AuNCs synthesized by Cluster Beam Deposition. Photocatalytic stearic acid degradation is achieved under UV and green light illumination. At an atomic equivalent Au cluster coverage of 2 ML and 4 ML, the photocatalytic activities of the TiO2 films under UV are not influenced by the presence of the AuNCs; however, the photocatalytic activities of these two films under green LED light, especially for the sample with 4 ML coverage, are greatly improved. Increasing the AuNC coverage to 8 ML does not lead to any further improvement of the photocatalytic activity, as it even starts to disrupt the photocatalytic activity. Altogether, this work presents a versatile and valuable strategy for the fabrication of noble metal modified photocatalytic surfaces with a high control over the cluster size and coverage, without using aggressive solvents nor organic ligands to reduce the negative effect of these molecules.
Acknowledgments
The research leading to these results has received funding from the European Union’s Seventh Framework Programme (FP7/2007-2013) under grant agreement n° 607417 (Catsense). We also thank the Research Foundation—Flanders (FWO, Belgium), the Flemish Concerted Action (BOF KU Leuven, Project No. GOA/14/007) research program, and the microscope was partly funded by the Hercules Fund from the Flemish Government for the support. N.C. and S.B. acknowledge financial support from European Research Council (ERC Starting Grant #335078-COLOURATOM).
Conflicts of Interest
The authors declare no competing financial interest.
References
Untitled section
References
- 1.Mills A., LeHunte S. An overview of semiconductor photocatalysis. J. Photochem. Photobiol. A. 1997;108:1–35. doi: 10.1016/S1010-6030(97)00118-4.
- 2.Wenderich K., Mul G. Methods, mechanism, and applications of photodeposition in photocatalysis: A review. Chem. Rev. 2016;116:14587–14619. doi: 10.1021/acs.chemrev.6b00327.
- 3.Ismail A.A., Bahnemann D.W., Bannat I., Wark M. Gold nanoparticles on mesoporous interparticle networks of titanium dioxide nanocrystals for enhanced photonic efficiencies. J. Phys. Chem. C. 2009;113:7429–7435. doi: 10.1021/jp900766g.
- 4.Mishra Y.K., Modi G., Cretu V., Postica V., Lupan O., Reimer T., Paulowicz I., Hrkac V., Benecke W., Kienle L., et al. Direct growth of freestanding ZnO tetrapod networks for multifunctional applications in photocatalysis, UV photodetection, and gas sensing. ACS Appl. Mater. Interface. 2015;7:14303–14316. doi: 10.1021/acsami.5b02816.
- 5.Grottrup J., Schutt F., Smazna D., Lupan O., Adelung R., Mishra Y.K. Porous ceramics based on hybrid inorganic tetrapodal networks for efficient photocatalysis and water purification. Ceram. Int. 2017;43:14915–14922. doi: 10.1016/j.ceramint.2017.08.008.
- 6.Mishra Y.K., Adelung R. ZnO tetrapod materials for functional applications. Mater. Today. :2017. doi: 10.1016/j.mattod.2017.11.003.
- 7.Reimer T., Paulowicz I., Roder R., Kaps S., Lupan O., Chemnitz S., Benecke W., Ronning C., Adelung R., Mishra Y.K. Single step integration of ZnO nano- and microneedles in Si trenches by novel flame transport approach: Whispering gallery modes and photocatalytic properties. ACS Appl. Mater. Interface. 2014;6:7806–7815. doi: 10.1021/am5010877.
- 8.Kato H., Kudo A. Visible-light-response and photocatalytic activities of TiO2 and SrTiO3 photocatalysts codoped with antimony and chromium. J. Phys. Chem. B. 2002;106:5029–5034. doi: 10.1021/jp0255482.
- 9.Sivula K., Le Formal F., Gratzel M. Solar water splitting: Progress using hematite (α-Fe2O3) photoelectrodes. ChemSusChem. 2011;4:432–449. doi: 10.1002/cssc.201000416.
- 10.Padhi D.K., Parida K. Facile fabrication of alpha-FeOOH nanorod/RGO composite: A robust photocatalyst for reduction of Cr(VI) under visible light irradiation. J. Mater. Chem. A. 2014;2:10300–10312. doi: 10.1039/C4TA00931B.
- 11.Jin J., Yu J.G., Guo D.P., Cui C., Ho W.K. A hierarchical Z-scheme CdS-WO3 photocatalyst with enhanced CO2 reduction activity. Small. 2015;11:5262–5271. doi: 10.1002/smll.201500926.
- 12.del Alamo J.A. Nanometre-scale electronics with III-V compound semiconductors. Nature. 2011;479:317–323. doi: 10.1038/nature10677.
- 13.Dhakshinamoorthy A., Navalon S., Corma A., Garcia H. Photocatalytic CO2 reduction by TiO2 and related titanium containing solids. Energy Environ. Sci. 2012;5:9217–9233. doi: 10.1039/c2ee21948d.
- 14.Luna A.L., Novoseltceva E., Louarn E., Beaunier P., Kowalska E., Ohtani B., Valenzuela M.A., Remita H., Colbeau-Justin C. Synergetic effect of Ni and Au nanoparticles synthesized on titania particles for efficient photocatalytic hydrogen production. Appl. Catal. B. 2016;191:18–28. doi: 10.1016/j.apcatb.2016.03.008.
- 15.Luna A.L., Dragoe D., Wang K.L., Beaunier P., Kowalska E., Ohtani B., Uribe D.B., Valenzuela M.A., Remita H., Colbeau-Justin C. Photocatalytic hydrogen evolution using Ni-Pd/TiO2: Correlation of light absorption, charge-carrier dynamics, and quantum efficiency. J. Phys. Chem. C. 2017;121:14302–14311. doi: 10.1021/acs.jpcc.7b01167.
- 16.Robert D., Malato S. Solar photocatalysis: A clean process for water detoxification. Sci. Total Environ. 2002;291:85–97. doi: 10.1016/S0048-9697(01)01094-4.
- 17.Lonnen J., Kilvington S., Kehoe S.C., Al-Touati F., McGuigan K.G. Solar and photocatalytic disinfection of protozoan, fungal and bacterial microbes in drinking water. Water Res. 2005;39:877–883. doi: 10.1016/j.watres.2004.11.023.
- 18.Wen M., Cheng M.Z., Zhou S.Q., Wu Q.S., Wang N., Zhou L.Y. Synthesis of reusable NiCo@Pt nanoalloys from icosahedrons to spheres by element lithography and their synergistic photocatalysis for nano-ZnO toward dye wastewater degradation. J. Phys. Chem. C. 2012;116:11702–11708. doi: 10.1021/jp2115912.
- 19.Lin H.X., Xu Z.T., Wang X.X., Long J.L., Su W.Y., Fu X.Z., Lin Q. Photocatalytic and antibacterial properties of medical-grade PVC material coated with TiO2 film. J. Biomed. Mater. Res. Part B. 2008;87B:425–431. doi: 10.1002/jbm.b.31120.
- 20.Verbruggen S.W. TiO2 photocatalysis for the degradation of pollutants in gas phase: From morphological design to plasmonic enhancement. J. Photochem. Photobiol. C. 2015;24:64–82. doi: 10.1016/j.jphotochemrev.2015.07.001.
- 21.Zhao X.J., Zhao Q.N., Yu J.G., Liu B.S. Development of multifunctional photoactive self-cleaning glasses. J. Non-Cryst. Solids. 2008;354:1424–1430. doi: 10.1016/j.jnoncrysol.2006.10.093.
- 22.Li J.T., Wu N.Q. Semiconductor-based photocatalysts and photoelectrochemical cells for solar fuel generation: A review. Catal. Sci. Technol. 2015;5:1360–1384. doi: 10.1039/C4CY00974F.
- 23.Hashimoto K., Irie H., Fujishima A. TiO2 photocatalysis: A historical overview and future prospects. Jpn. J. Appl. Phys. Part 1. 2005;44:8269–8285. doi: 10.1143/JJAP.44.8269.
- 24.Verbruggen S.W., Keulemans M., Goris B., Blommaerts N., Bals S., Martens J.A., Lenaerts S. Plasmonic ‘rainbow’ photocatalyst with broadband solar light response for environmental applications. Appl. Catal. B. 2016;188:147–153. doi: 10.1016/j.apcatb.2016.02.002.
- 25.Verbruggen S.W., Keulemans M., Filippousi M., Flahaut D., Van Tendeloo G., Lacombe S., Martens J.A., Lenaerts S. Plasmonic gold-silver alloy on TiO2 photocatalysts with tunable visible light activity. Appl. Catal. B. 2014;156:116–121. doi: 10.1016/j.apcatb.2014.03.027.
- 26.Kafizas A., Kellici S., Darr J.A., Parkin I.P. Titanium dioxide and composite metal/metal oxide titania thin films on glass: A comparative study of photocatalytic activity. J. Photochem. Photobiol. A. 2009;204:183–190. doi: 10.1016/j.jphotochem.2009.03.017.
- 27.Tahir M., Tahir B., Amin N.A.S. Synergistic effect in plasmonic Au/Ag alloy NPs co-coated TiO2 NWs toward visible-light enhanced CO2 photoreduction to fuels. Appl. Catal. B. 2017;204:548–560. doi: 10.1016/j.apcatb.2016.11.062.
- 28.Kamimura S., Yamashita S., Abe S., Tsubota T., Ohno T. Effect of core@shell (Au@Ag) nanostructure on surface plasmon-induced photocatalytic activity under visible light irradiation. Appl. Catal. B. 2017;211:11–17. doi: 10.1016/j.apcatb.2017.04.028.
- 29.Mrowetz M., Villa A., Prati L., Selli E. Effects of Au nanoparticles on TiO2 in the photocatalytic degradation of an azo dye. Gold Bull. 2007;40:154–160. doi: 10.1007/BF03215573.
- 30.Pauwels B., Van Tendeloo G., Zhurkin E., Hou M., Verschoren G., Kuhn L.T., Bouwen W., Lievens P. Transmission electron microscopy and Monte Carlo simulations of ordering in Au-Cu clusters produced in a laser vaporization source. Phys. Rev. B. 2001;63:165406. doi: 10.1103/PhysRevB.63.165406.
- 31.Galhenage R.P., Yan H., Tenney S.A., Park N., Henkelman G., Albrecht P., Mullins D.R., Chen D.A. Understanding the nucleation and growth of metals on TiO2: Co compared to Au, Ni, and Pt. J. Phys. Chem. C. 2013;117:7191–7201. doi: 10.1021/jp401283k.
- 32.Akita T., Lu P., Ichikawa S., Tanaka K., Haruta M. Analytical TEM study on the dispersion of Au nanoparticles in Au/TiO2 catalyst prepared under various temperatures. Surf. Interface Anal. 2001;31:73–78. doi: 10.1002/sia.959.
- 33.Mills A., Wang J.S. Simultaneous monitoring of the destruction of stearic acid and generation of carbon dioxide by self-cleaning semiconductor photocatalytic films. J. Photochem. Photobiol. A. 2006;182:181–186. doi: 10.1016/j.jphotochem.2006.02.010.
- 34.Allain E., Besson S., Durand C., Moreau M., Gacoin T., Boilot J.P. Transparent mesoporous nanocomposite films for self-cleaning applications. Adv. Funct. Mater. 2007;17:549–554. doi: 10.1002/adfm.200600197.
- 35.Verbruggen S.W., Masschaele K., Moortgat E., Korany T.E., Hauchecorne B., Martens J.A., Lenaerts S. Factors driving the activity of commercial titanium dioxide powders towards gas phase photocatalytic oxidation of acetaldehyde. Catal. Sci. Technol. 2012;2:2311–2318. doi: 10.1039/c2cy20123b.
- 36.Hurum D.C., Agrios A.G., Gray K.A., Rajh T., Thurnauer M.C. Explaining the enhanced photocatalytic activity of degussa p25 mixed-phase TiO2 using EPR. J. Phys. Chem. B. 2003;107:4545–4549. doi: 10.1021/jp0273934.
- 37.Murdoch M., Waterhouse G.I.N., Nadeem M.A., Metson J.B., Keane M.A., Howe R.F., Llorca J., Idriss H. The effect of gold loading and particle size on photocatalytic hydrogen production from ethanol over Au/TiO2 nanoparticles. Nat. Chem. 2011;3:489–492. doi: 10.1038/nchem.1048.
- 38.Caretti I., Keulemans M., Verbruggen S.W., Lenaerts S., Van Doorslaer S. Light-induced processes in plasmonic gold/TiO2 photocatalysts studied by electron paramagnetic resonance. Top. Catal. 2015;58:776–782. doi: 10.1007/s11244-015-0419-4.
- 39.Linic S., Christopher P., Ingram D.B. Plasmonic-metal nanostructures for efficient conversion of solar to chemical energy. Nat. Mater. 2011;10:911–921. doi: 10.1038/nmat3151.
- 40.Priebe J.B., Karnahl M., Junge H., Beller M., Hollmann D., Bruckner A. Water reduction with visible light: Synergy between optical transitions and electron transfer in Au-TiO2 catalysts visualized by in situ epr spectroscopy. Angew. Chem. Int. Ed. 2013;52:11420–11424. doi: 10.1002/anie.201306504.
- 41.Ferrari P., Vanbuel J., Li Y., Liao T.-W., Janssens E., Lievens P. Gas-Phase Synthesis of Nanoparticles. Wiley-VCH Verlag GmbH & Co. KGaA; Weinheim, Germany: 2017. The double-laser ablation source approach; pp. 59–78.
- 42.Paz Y., Luo Z., Rabenberg L., Heller A. Photooxidative self-cleaning transparent titanium-dioxide films on glass. J. Mater. Res. 1995;10:2842–2848. doi: 10.1557/JMR.1995.2842.